Engineering, 21.06.2021 15:40 DeonDub3106

A test bar of nonferrous material has a diameter of 0.253 inches. Upon applying a tensile load, the sample exhibited 0.002 plastic strain at 3400 lb and the maximum load during testing was 6200 lb and occurred at an engineering strain of 0.65; and breaking occurred at 4400 lb. The sample diameter at fracture was measured to be 0.15 inches. Required:
a. The yield strength of the material is :
b. The UTS of the material is:

Answers: 2

Show answers

Another question on Engineering

Engineering, 04.07.2019 18:10

The thermal expansion or contraction of a given metal is a function of the f a)-density b)-initial temperature c)- temperature difference d)- linear coefficient of thermal expansion e)- final temperature f)- original length

Answers: 2

Answer

Engineering, 04.07.2019 18:20

Atank with constant volume contains 2.27 kg of a mixture of water phases (liquid-vapor). in the initial state the temperature and the quality are 127 °c and 0.6, respectively. the mixture is heated until the temperature of 160 oc is reached. illustrate the process in a t-v diagram. then, determine (1) the mass of the vapor in kg at the initial state, (2) the final pressure in kpa.

Answers: 3

Answer

Engineering, 06.07.2019 02:30

A12 mm diameter shaft runs in a plain cylindrical bush 30 mm long that is located in an 18 mm diameter hole in a housing. the shaft-inner bush fit is h8 f and the outer bush-housing fit is h7-p6. make a fully cimensioned sketch of the bush with tolerances. find the maximum and minimum clearance or interference for both fits on the inner and outer diameters of the bush

Answers: 3

Answer

Engineering, 06.07.2019 03:20

Not a characteristic property of ceramic material (a) high temperature stability (b) high mechanical strength (c) low elongation (d) low hardness

Answers: 2

Answer

You know the right answer?

A test bar of nonferrous material has a diameter of 0.253 inches. Upon applying a tensile load, the...

Questions