A cylindrical rod of brass originally 10 mm in diameter is to be cold worked by drawing. The circular cross section will be maintained during deformation. A cold-worked tensile strength in excess of 380 MPa and a ductility of at least 15 %EL are desired. Furthermore, the final diameter must be 7.5 mm. Explain how this may be accomplished. Use the graphs given in previous question.

Explanation:

From the information given:

original diameter = 10 mm

final diameter 7.5 mm

Cold work tensile strength of brass = 380 MPa

Recall that;

→ At 43.87% CW, Brass has a tensile strength of around 550 MPa, which is greater than 380 MPa.

→ At 43.87% CW, the ductility is less than 5% EL, As a result, the conditions aren't met.

To achieve 15% EL, 28% CW is allowed at most

i.e

The lower bound cold work = 15%

The upper cold work = 28%

The average = = 21.5 CW

Now, after the first drawing, let the final diameter be ; Then:

By solving:

To meet all of the criteria raised by the question, we must first draw a wire with a diameter of 8.46 mm and then 21.5 percent CW on it.

answer:

person b

explanation: